Product Description
High Temperature Application PTFE Heat Shrink Tube
High Temperature Application PTFE Heat Shrink Tube is made by Teflon materials (PTFE), Teflon Shrink Tubing can be used in 260 degrees C high temperature environment. Wear-proof, anti-oil, anti chemical corrosion and high temperature resistance. Teflon Cable Shrink Sleeve has superior flame resistance and physical-chemical properties, low friction coefficient.
Flexible Teflon tubing it has been widely used in high temperature wire harnesses, insulating protection to joint and weld, pressure to lift and identification to the covered components, as well as automobile, military, aerospace and aviation, etc.
Rohs High temperature application PTFE heat shrink tube wrap in the chemical components may be preventing oil, acid and basic resistance; wrap in the electrical components can have excellent high and low temperature resistance, electrical insulation; wrap in the printing and dyeing, paper, printing, chemical and other industries on the roller can have a lubricating, non-viscous; wrap movement in the complex mechanical components, will be extremely low friction coefficient, smooth running, and avoid "to grasp" and so on. Teflon Heat Shrink Tubing widely used in electrical, chemical, mechanical, and printing industries.
LED & Fluorescent Lamp Protection Sleeves, This product expansion before blowing through the United States based on the UL certification, RoHS high temperature application ptfe heat shrink tube retains the excellent performance of PTFE tube and increased heat shrinkable special features .
Features & Benefits
1, Heat shrink ratio: 1.7:1, 4:1
2, High flame resistance, superior electrical-chemical properties.
3, Low friction coefficient.
4, RoHs compliant.
Up to standard: Approvals
Meet SAE-AMS-DTL-23053/12
Operating indexes:
Max. Shrink temp.:350 degrees C
Operating temp.: -65 degrees C~260 degrees C
|
Product Property
|
Performance requirements
|
Product Property
|
Performance requirements
|
|
Specific gravity g/cm3
|
2.10
|
Min. Shrink temp.
|
300℃
|
|
Tensile strength Mpa
|
20.5
|
Miz. Shrink temp.
|
350℃
|
|
Bending strength Mpa
|
400
|
Absorptivity
|
≤0.01%
|
|
Impact strength
|
-NO Break
|
Longitudinal shrinking ratio(%)
|
≤5%
|
|
Hardness ShoreD
|
85
|
Elongation at break(%)
|
330
|
|
Friction coefficient
|
0.1
|
Aging in air oven
|
300℃
|
|
Flammability
|
VW-1
|
0.5
|
2
|
|
After heat aging
|
Tensile strength(Mpa)
|
20
|
|
Dielectric constant
|
2.1
|
Elongation at break(%)
|
200
|
|
Dissipation Factor
|
0.0002
|
Volume resistivity (Ω/cm)
|
>1018
|
|
Arc coefficient
|
>300
|
Breakdown strength(KV/mm)
|
30
|
|
Weather ability
|
NO Break
|
Flammability
|
VW-1
|
|
Resistance to chemical attack
|
Excellent
|
Concentricity rate(%)
|
≥60
|
Colors: Blue, transparent ( other colors can be customized )
.png)
Contact Now